SPECIFICATIONS

High Clear Resin

Crystal and Clear

Resist Yellowing, Highly Transparent, Tough and Resilient

Specifications

Wavelength 365-405nm               Elongation at break 14.6%
Density 1.05-1.25 g/cm3              Shrinkage 3.72-4.24%
Viscosity ： 266 cPormPa·s        Flexural strength 30.3 MPa
Surface hardness 78 HS             Flexural modulus 798 MPa
Tensile strength 28.1 MPa           Yellowing resisting time >30 Minutes
Conservation period 12 Months   Resin wash Alcohol

Highly Transparent and Long-lasting Clarity

Model Varnishing

1. Model support removal
2. Alcohol wash
3. Apply High Clear Resin/varnish
4. Cure for 2 minutes

Tough and Resilient

A 100% rise in resilience compared to standard resin,
making the prints and models less easy to break.

Light Odor and Safe

The High Clear Resin has a light odor and is less irritating ,
bringing users a better and safer printing experience.

Precautions

1. Store at room temperature, keep sealed and away from light. Avoid heat and direct sunlight.

2. Suggested storage temperature: 18-35℃.
Lowtemperatures might affect the printing results. The resin can be preheated (no more than 60C) before use. In case ofresin pigment settlement, please stir or shake well before use.

3. To ensure the best properties of the cured models, remember to control
the intensity and the exposure time of the light source.
To ensure the ideal curing material performance, the post-curing light intensity and time need to be controlled as suggested:
(1) The intensity of lamps or LED light source should not exceed 5-10mW/cm² and the exposition time should not exceed 1 hour (self-regulation);
(2) Close range exposure or prolonged exposure under strong light sources such as high power and high voltage lamp is prohibited.
(3) It is recommended to print in a dark room or put on the cover when printing.

Material performance may vary and is subject to the machine used and
post-curing technique. Please refer to the product MSDS for safety information. If you have any problems or questions, please feel free to contact us.